Cast coated label paper:

CAST COATED PAPER ARCADIA 2000 / SB4ARLUX 8000 (ROLL ORDER)

No	PARAMETER	UNIT		80 GSM	85 GSM	90 GSM	100 GSM 100 ±3	TEST METHOD
1	Basis Weight	Gsm		80 ±3	85 ±3	90 ±3		T410om-98
2	Thickness	Micron		88 ±5	95 ±5	100 ±5	110 ±5	T 411 ora-97
3	Roughness	Micron	Coated	Max. 1.0	Max. 1.0	Max. 1.0	Max. 1.0	T 555 om-94
4	Tensile Strength	kgf/15mm	CD	Min. 3.5	Min. 3.5	Min. 3.9	Min. 4.2	T 494 om-96
			MD	Min. 6.0	Min. 7.0	Min. 7.2	Min. 9.0
5	Tear Strength	grf	CD	Min. 40	Min. 45	Min. 50	Min. 55	T414 om-98
			MD	Min. 35	Min. 40	Min. 45	Min. 50
6	ISO Brightness	%	Coated	88±2	88±2 r	88 ±2	88 ±2	ISO 2470-1977
7	CIE Whiteness	%	Coated	101 ±2	101 ±2	101 ±2	101 ±2	-
8	ISO Opacity	%		Min. 89	Min. 90	Min. 91	Min. 92	T 519 om-96
9	Surface pH		Coated	7.0 ± 0.5	7.0 ± 0.5	7.0 ±0.5	7.0 ±0.5	-
			Uncoated	7.0 ± 0.5	7.0 ± 0.5	7.0 ±0.5	7.0 ± 0.5
10	Cobb/60 sec	Gsm	Uncoated	20 ±5	20 ±5	20±5	20 ±5	T 441 om-98
11	IGT Pick Test	m/s	Coated	Min. 0.7	Min. 0.7	Min. 0.7	Min. 0.7	IGT Method W31
12	Gloss 75	%	Coated	88 ±5	88 ±5	88 ±5	88 ±5	T 480 om-92
13	Set Off	D	Coated	0.20 ±0.08	0.20 ± 0.08	0.20 ± 0.08	0.20 ± 0.08	-
14	Moisture Paper *	%		5 ± 0.5	5 ± 0.5	5 ± 0.5	5 ± 0.5	T 412 om-94

CAST COATED PAPER ARCADIA 2000 / SINARLUX 8000 (SHEET ORDER)

NO	PARAMETER	UNIT	80 GSM	85 GSM	90 GSM		100 GSM
1	Basis Weight	Gsm		80 ±3	85 ±3	90 ±3	100 ±3
2	Thickness	Micron		88 ±5	95 ±5	100 ±5	110±5
3	Roughness	Micron	Coated	Max. 1.0	-lax. 1.0	Max. 1.0	Max. 1.0
4	Tear Strength	grf	CD	Min. 40	Vtin. 45	Min. 50	Min. 55
			MD	Min. 35	Win. 40	Min. 45	Min. 50
5	ISO Brightness	%	Coated	88 ±2	88 ± 2	88 ±2	88 ±2
6	CIE Whiteness	%	Coated	101±2	101 ±2	101 ±2	101 ±2
7	ISO Opacity	%		Min. 89	Min. 90	Min. 91	Min. 92
8	Surface pH	-	Coated	7.0 ±0.5	J.O ± 0.5	7.0 ±0.5	7.0 ±0.5
			Uncoated	7.0 ±0.5	7.0 ±0.5	7.0 ±0.5	7.0 ± 0.5
9	Cobb/60 sec	Gsm	Uncoated	20 ±5	20 ±5	20±5	20 ±5
10	IGT Pick Test	ra/s	Coated	Min. 0.7	Min. 0.7	Min. 0.7	Min. 0.7
11	Gloss 75	%	Coated	88 ±5	88 ±5	88 ±5	88 ±5
12	Set Off	D	Coated	0.20 ± 0.08	20 ± 0.08	0.20 ±0.08	0.20 ± 0.08
13	Moisture Paper	%		5 ± 0.5	5 ± 0.5	5 ± 0.5	5 ± 0.5